Exhaust valve Materials and Treatments

Material Requirements.
  • The material should retain its greatest strength at high temperatures.
  • No tendencies to air harden.
  • Critical temperature above 800*C.
  • No tendency of high temperature scaling.
  • Hot and cold corrosion resistant.
  • Able to be forged and machined easily.
  • Capable of consistent and reliable heat treatment.
  • Most diesel engines use an Austenitic heat-resisting alloy steel. The seating surface can be stellited.
Typical heat treatment: 
  • Heat up to 950*C and cool in air to give a Brinnel Hardness of 269.
Surface Treatment:
  • Surface treatment is frequently used to improve or modify valve steel characteristics. Chrome-cobalt-tungsten alloy available in various grades of hardness is widely used.
  • The hardness when deposited is in the order of 375 to 425 Brinnel.
  • The valve head is treated to more than 430*C to reduce contraction stresses.
  • The value face is now sweated by an oxyacetylene flame and the alloy deposited continually by welding (1.02 mm to 1.52 mm).
Valve Seat Inserts:
  • Alloy Irons, with high percentage of molybdenum and Chromium with a Brinnel number of Approx. 500 are best.
  • Alloy steel with stellited seating surface are also in common use.
  • The methods employed for fitting the inserts include screwing and shrinking.
Valve Guides:
  • Valve guides are mostly made of Cast Iron.
  • To avoid scaling etc at high temperatures alloy Irons are preferred.
  • Phosphor Bronze and Gun metal have also been successfully used.
  • Alloy Iron guides with Bronze linings also are in common use.
Valve Housing:
  • Mostly made of pearlitic cast iron and provided with a chamber for cooling water.
Labels:

Comments

Post a Comment

If you have any doubts.Please let me know

Popular posts from this blog

Main engine interlocks

Interlocks are provided so that the engine can be started or reversed only when certain conditions have been fulfilled. When there is a remote control of engines, it is essential to have interlocks. This reduces the possibility of engine damage and any hazards to the operating personnel. Turning gear Interlock . This device prevents the engine from being started if the Turning gear is engaged. Running Direction Interlock . This prevents the fuel from being supplied if the running direction of the engine does not match the Telegraph. Starting Air Distributor in end position . This prevents starting from taking place if the shifting of the Distributor has not been completed. Main Lube. oil pressure, Piston cooling pressure, Jacket water pressure, and important parameters must be above the required minimum. Auxiliary Blower Interlock . The Auxiliary Blower is provided in case of Constant pressure turbo charging. Air Spring pressure Interlock . In case of the present generation...
8 comments
Read more

Differences between MC/MC-C and ME/ME-C engines

The electrohydraulic control mechanisms of the ME engine replace the following components of the conventional MC engine: Chain drive for camshaft Camshaft with fuel cams, exhaust cams and indicator cams Fuel pump actuating gear, including roller guides and reversing mechanism Conventional fuel pressure booster and VIT system Exhaust valve actuating gear and roller guides Engine driven starting air distributor Electronic governor with actuator Regulating shaft Engine side control console Mechanical cylinder lubricators. The Engine Control System of the ME engine comprises: Control units Hydraulic power supply unit Hydraulic cylinder units, including: Electronically controlled fuel injection, and Electronically controlled exhaust valve activation Electronically controlled starting air valves Electronically controlled auxiliary blowers Integrated electronic governor functions Tacho system Electronically controlled Alpha lubricators
15 comments
Read more

Manganese bronze is not typically used as a propeller material .Why

1. High cost: Manganese bronze is a costly alloy, making it less economical for large propellers. 2. Low strength-to-weight ratio: Compared to other propeller materials like nickel-aluminum bronze or stainless steel, manganese bronze has a lower strength-to-weight ratio. 3. Susceptible to corrosion: Manganese bronze can corrode in seawater, especially when exposed to high velocities and turbulence. 4. Poor cavitation resistance: Manganese bronze is more prone to cavitation damage than other materials. 5. Difficult to cast and machine: Manganese bronze is challenging to cast and machine, making it less desirable for complex propeller geometries. 6. Limited weldability: Manganese bronze has poor weldability, making repairs and modifications difficult. Nickel-aluminum bronze or stainless steel are commonly used for propellers due to their: - High strength and durability - Excellent corrosion resistance - Good cavitation resistance - Ease of casting and machining - Weldability
88 comments
Read more